Bearing steel shot peening is a cold working process

2016-01-04 16:42:33   Review:0 Click:

  Bearing  steel shot peening is a cold working process in which small spherical media called shot bombard the surface of a part. During the bearing shot peening process, each piece of shot that strikes the material acts as a tiny peening hammer, imparting to the surface a small indentation or dimple. To create the dimple, the surface of the material must yield in tension. Below the surface, the material tries to restore its original shape, thereby producing below the dimple, a hemisphere of cold-worked material highly stressed in compression.

  Nearly all fatigue and stress corrosion failures originate at the surface of a part, but cracks will not initiate or propagate in a compressively stressed zone. Because the overlapping dimples from shot peening create a uniform layer of compressive stress at metal surfaces, bearing shot peening provides considerable increases in part life. Compressive stresses are beneficial in increasing resistance to fatigue failures, corrosion fatigue, stress corrosion cracking, hydrogen assisted cracking, fretting, galling and erosion caused by cavitation. The maximum compressive residual stress produced just below the surface of a part by shot peening is at least as great as one-half the yield strength of the material being shot peened.

  Hebei Reaguan International Co.,Ltd is a leading manufacturer and supplier of cast grits and steel cut wire manufacture.

An article:Sandblasting equipment is used for surface finishing processing
The next one:the common denominator is tensile stress

<View all>
I'll say somethingAlready existing0Comment,Click to view all

REAGUAN
Tel:+86-317-5295077    Fax:+86-317-5295979   Email:sale@reaguan.cn Add:YiheBuilding,CangzhouCity,Hebei Province   Copyright © Hebei Reaguan International Co.,ltd.  Technical Support:boyikeji  Technical support: BOYIKEJI