The formed cut wire shot is reheated to purify evenly

2021-05-21 11:25:24   Review:0 Click:
  Cut wire shot is also widely used in the casting industry. When the workpiece is taken out of the mold, the grit on the surface of the workpiece is removed with cut wire shot. When cut wire shot is used with suitable equipment, because it is durable, it is definitely the best abrasive for your surface cleaning. The manufacturing process of cut wire shot is as follows: firstly, melt high-quality steel block, then spray high-pressure water to make molten steel form particles, reheat the formed cut wire shot to purify evenly, and then quench. Because the surface color of tempered iron shot is even blue after annealing, it is often used as cast steel shot. The service life of iron shot is only 50-400 times. The rust removal effect of iron shot is seriously reduced and the interests of users are seriously damaged.

  Products with different particle size and hardness are used in different processes, such as surface strengthening. Workpiece coating, workpiece bonding pretreatment sand blasting can remove all the dirt on the surface of the workpiece, such as rust, cut wire shot and establish a very important basic schema on the surface of the workpiece, and can achieve different degrees of roughness by changing abrasive of different particle sizes, greatly improving the adhesion of the workpiece and coating, plating. Cut wire shot is used for steel plate pretreatment, generally used for rust removal before coating.

  There are many kinds of cut wire shot. Different cut wire shot needs different raw materials and equipment. Production of cut wire shot, there are also related production lines and equipment, can be purchased directly. There are many places where cut wire shot is needed, such as casting, forging, surface treatment of machined parts, surface treatment of parts after heat treatment, etc., which can be sold to these related places, such as general manufacturing, shipbuilding, etc., and the general heavy industry will have some demand.

  Advanced casting technology and equipment: the international advanced anhydrous production process is adopted, that is, completely dry resin sand is applied on the metal film to completely eliminate the casting defects such as porosity and slag inclusion caused by water glass moisture, so that the product quality has a qualitative leap; Moreover, the ratio of iron to carbon is improved to meet the requirements of quenching.

An article:Classification of cast steel shot by hardness
The next one:Use cast steel grits as abrasive and counterweight to use wear degree

<View all>
I'll say somethingAlready existing0Comment,Click to view all

REAGUAN
Tel:+86-317-5295077    Fax:+86-317-5295979   Email:sale@reaguan.cn Add:YiheBuilding,CangzhouCity,Hebei Province   Copyright © Hebei Reaguan International Co.,ltd.  Technical Support:boyikeji  Technical support: BOYIKEJI